offered by RECETA from import
- Fluorspar:
- metallurgical grade, CaF2 min 90%, size 10-70mm and 10-150(200)mm
- cement grade, CaF2 min 85%, size 0-15mm
- for welding electrodes and chemical industry, CaF2 min 97%, size 0-15mm
- Round Kiln Bauxite - metallurgical grade, Al2O3 min 89%, bulk density 3.30 g/cm³ min, size 5-30mm 90% min
- Round Kiln Bauxite - refractory grade, Al2O3 min 89%, Fe2O3 1.7% max, bulk density 3.35 g/cm³ min, sizes:
- 0-30mm
- 3-6mm
- 1-3mm
- 0-1mm
- 325mesh
- Raw Bauxite, Al2O3 min 85% (in calcined state), L.O.I. 14-15%
- Kaolin (China Clay) - natural, 45% Al2O3 min (in calcined state), Fe2O3 0.4%, L.O.I. 14.5%, size 0-10mm, optional 125, 250 and 325 mesh
- Magnesites:
- calcined (caustic), CM 94
- dead burn, DBM 90, DBM 95, DBM 97.5%
- electro fused, EFM 97.5%
- White fused alumina (W.F.A.), Al2O3 min 99.8%, sizes:
- 3-5mm
- 1-3mm
- 0-1mm
- 0-0.5mm
- 0-0.074mm
- 0-0.063mm
and other optionalsizes
- Brown fused alumina (B.F.A.),Al2O3 min 96%, sizes:
- 3-5mm
- 1-3mm
- 0-1mm
- 0-0.5mm
- 0-0.074mm
- 0-0.063mm
and other optionalsizes
- Reactive alumina, Al2O3 min 99.8%, size <1 m 90% min
- Zirconium sand/flour, ZrO2 min 65%, optionalsizes
- Refractory, High Alumina Cement, HAC 80, HAC 70, HAC 55
- Silicon carbide, SiC min 97%, sizes:
- 0-0.1mm
- 0.1-1mm
- 1-3mm
and other optionalsizes
- Ferroalloys:
- Ferromanganese, FeMn 75 standard, FeMn 75/85 affine
- Ferrosilicon, FeSi 75, FeSi 65, FeSi 45
- Ferrochrome, FeCr 65 standard
- Silica fume, SiO2 min 96%, size <1 m 90% min
- REFRAMUL, Al2O3 45%, 60%, 70%, bulk density 2.5, 2.65 and 2.85 g/cm³ min respectively.
- Light weight chamotte, Al2O3 45%, 60%, 70%, bulk density 0.8% g/cm³ max
- Refractory bricks, special quality:
- light weight (insulating for high temperature)
- high alumina
- basic (magnesia, magnesia-chrome, magnesia-carbon, etc.)